MASTER ALLOYS

 

Copper Phosphorous

 

GERMANY-DIN 17657

 

Copper Alloys		P	CU	P+CU Min	FE	NI	PB	SN	ZN	SB	MN	AL	SI
V - CuP10	(2.1631)	9.5-11	89 Min	-	0.15	0.2	0.2	0.2	0.2	-	-	-	-
VR - CuP10	(2.1633)	9.5-11	89 Min	-	0.05	0.1	0.03	0.05	0.05	0.01	-	-	-
DIN 8513
L-CuP8	(2.1465)	7.6-8.4	Rem.	-	-	-	0.02	-	-	-	-	0.01	-
L-CuP7	(2.1463)	6.7-7.5	Rem.	-	-	-	0.02	-	-	-	-	0.01	-
L-CuP6	(2.1462)	5.9-6.5	Rem.	-	-	-	0.02	-	-	-	-	0.01	-

 

JAPAN-JIS H2501

 

Copper Alloys	P	CU	P+CU Min	FE	NI	PB	SN	ZN	SB	MN	AL	SI
1A 15 P Cu A	14.5 Min	Rem.	99.75	0.05	-	0.01	0.01	-	-	-	-	-
1B 15 P Cu B	14 Min	Rem.	99.75	0.15	-	-	-	-	-	-	-	-
2 10 p Cu	10-11	Rem.	99.75	0.15	-	-	-	-	-	-	-	-
3 8 P Cu	8-9	Rem.	99.75	0.15	-	-	-	-	-	-	-	-

 

EUROPEAN STANDARD

 

Copper Alloys		P	CU	P+CU Min	FE	NI	PB	SN	ZN	SB	MN	AL	SI
Cu P 15 A	CM217E	13.5-15	84.5 Min	-	0.1	0.1	0.03	0.05	0.05	0.01	0.1	0.02	0.05
Cu P 15 B	CM218E	13.5-15	84 Min	-	0.1	0.1	0.1	0.1	0.1	-	-	-	-
Cu P 15 C	CM219E	13.5-15	83.5 Min	-	0.2	0.2	0.2	0.2	0.2	-	-	-	-
Cu P 10 A	CM215E	9.5-11	88.5 min	-	0.1	0.1	0.03	0.05	0.05	0.01	0.1	0.02	0.05
Cu P 10 B	CM215E	9.5-11	87.5 Min	-	0.2	0.2	0.2	0.2	0.2	-	-	-	-

 

USA - ASTM B-52

 

Copper Alloys	P	CU	P+CU Min	FE	NI	PB	SN	ZN	SB	MN	AL	SI
Alloy A	14 Min	Rem.	99.75	0.15	0.15	-	-	-	-	-	-	-
Alloy B	10 Min	Rem.	99.75	0.15	0.15	-	-	-	-	-	-	-